A facile route for graphene oxide (GO) paper production

It is demonstrated that graphene oxide (GO) paper outperforms many other paper-like materials (especially ‘bucky paper’) in stiffness and strength, which can result from the unique interlocking-tile arrangement of the nanoscale GO sheets. This fascinating free-standing paper-like material holds great potentials in many fields, such as protective layers, chemical filters, components of electrical batteries or supercapacitors, adhesive layers, and composite applications, etc.

A facile route for the large scale production of GO papers and their mechanical enhancement has been presented by Zhang et al. The novel paper-like GO made from individual GO sheets in aqueous suspension can be achieved in large scale by a simple solvent-casting method on hydrophobic substrates. Significant enhancement in mechanical stiffness (341%) and fracture strength (234%) of GO paper have been achieved upon modification with a small amount (less than 10 wt%) of glutaraldehyde (GA). The cross-linking reaction takes place between hydroxyl groups on the surface of GO and aldehyde groups of GA, through forming hemiacetal structure, which can result in distinct mechanical enhancement of the GO papers.

You can find out more about their work by reading the article in Nano-Micro Letters which is free to access.


Nantao Hu, Lei Meng, Rungang Gao, Yanyan Wang, Jing Chai, Zhi Yang, Eric Siu-Wai Kong and
Yafei Zhang, “A Facile Route for the Large Scale Fabrication of Graphene Oxide Papers and Their Mechanical
Enhancement by Cross-linking with Glutaraldehyde”, Nano-Micro Lett. 3 (4), 215-222 (2011). http://dx.
doi.org/10.3786/nml.v3i4.p215-222

Tags: 
Subscribe to Comments RSS Feed in this post

23 Responses

  1. you are really a good webmaster. The website loading speed is incredible. It seems that you are doing any unique trick. Moreover, The contents are masterpiece. you have done a fantastic job on this topic!

  2. Nice to read your blog

  3. I just want to mention I am very new to blogs and seriously enjoyed you’re web-site. Probably I’m planning to bookmark your site . You absolutely come with outstanding stories. Bless you for sharing with us your webpage.

  4. WONDERFUL Post.thanks for share..more wait .. …

  5. I was more than happy to find this web-site.I needed to thanks for your time for this glorious read!! I undoubtedly having fun with every little little bit of it and I have you bookmarked to check out new stuff you blog post.

  6. I love your useful blog. super work. I hope you release many. I will carry on watching

  7. I have never ever imagined that studying can be so significantly exciting.

  8. I have never ever imagined that studying can be so significantly exciting.

  9. Great article! I loved the knowledge and the information given . Plus, your article writing style is very fun to read. If you have time kindly browse my brand new website and let me know what you think.

  10. Your article is an excellent example of great writing. Your viewpoints are introduced clearly with intelligent commentary. I agree with many of your innovative ideas. It’s obvious that you know your topic. You are talented.

  11. Ybiv4S wow, awesome blog article.Really looking forward to read more. Really Cool.

  12. Great article! I loved the insight and advice given. In addition, your writing style is very pleasing to read. If you have time kindly explore my new webpage and let me know what you think.

  13. Another great post. I really enjoy it every time I visit this site. I’s obvious that a lot of time and effort is be put into every post and the entire website as a whole. Just wanted to let you know much I enjoy this place and prevaricate it, Thank again. Cheers!

  14. You had some good ideas there. I made a search on the issue and noticed most peoples will agree with your blog. Ensure to ask about things such as whether people liked the book, whether the plot worked for them, and the different themes they encountered in the book.

  15. You certainly have some agreeable opinions and views. nmstr.org provides a fresh look at the subject.

  16. I am not real superb with English but I get hold this very easy to understand .

  17. you are truly a good webmaster. The website loading velocity is amazing. It kind of feels that you are doing any unique trick. Also, The contents are masterwork. you’ve done a wonderful activity on this topic!

  18. I’m impressed!!! Really informative blog post on nmstr.org my friend. I just wanted to comment u0026 say keep up the quality work. best regards

  19. Usually I don’t read article on blogs, but I would like to say that this write-up very forced me to try and do it! Your writing style has been amazed me. Thanks, very nice post.. regards!

  20. wonderful put up, very informative. I’m wondering why the opposite specialists of this sector don’t understand this. You must continue your writing. I’m sure, you have a great readers’ base already!. regards!

Leave a Reply

Your email address will not be published. Required fields are marked *

*
*


*